Degradation of phenyl C61 butyric acid methyl ester: poly (3-hexylthiophene) organic photovoltaic cells and structure changes as determined by defect investigations

Thien-Phap Nguyen; Cedric Renaud; Frédéric Reisdorffer; Lee-Jyi Wang

doi:10.1117/1.JPE.2.021013

12 September 2012 Degradation of phenyl C61 butyric acid methyl ester: poly (3-hexylthiophene) organic photovoltaic cells and structure changes as determined by defect investigations

Thien-Phap Nguyen, Cedric Renaud, Frédéric Reisdorffer, Lee-Jyi Wang

Author Affiliations +

Journal of Photonics for Energy, Vol. 2, Issue 1, 021013 (September 2012). https://doi.org/10.1117/1.JPE.2.021013

Abstract

Stability of organic photovoltaic cells is the key issue for their commercialization. Despite intensive investigations to clarify the causes of failure of devices, the process of degradation is not yet well understood. In this work, we made use of the trap measurements by the charge-based deep-level transient spectroscopy to study devices that have been aged by continuous exposure to artificial sunlight for 20 h, and we compared the trap parameters to those obtained in freshly prepared samples. With regard to poly (3-hexylthiophene) (P3HT)-based devices, the P3HT:phenyl C61 butyric acid methyl ester blend cells showed an additional deep trap level and a higher trap density. In the degraded devices, all the existing traps in the fresh sample were found, and there was no creation of additional defect levels. The density of several trap levels in the polymer was strongly reduced after aging. Analysis of the results suggests that a phase separation in the photoactive blend has occurred, leading to a better organization of the polymer domains to lower defect states.

Citation Download Citation

Thien-Phap Nguyen, Cedric Renaud, Frédéric Reisdorffer, and Lee-Jyi Wang "Degradation of phenyl C61 butyric acid methyl ester: poly (3-hexylthiophene) organic photovoltaic cells and structure changes as determined by defect investigations," Journal of Photonics for Energy 2(1), 021013 (12 September 2012). https://doi.org/10.1117/1.JPE.2.021013

Published: 12 September 2012

ACCESS THE FULL ARTICLE

INSTITUTIONAL
Select your institution to access the SPIE Digital Library.

SELECT YOUR INSTITUTION

PERSONAL
Sign in with your SPIE account to access your personal subscriptions or to use specific features such as save to my library, sign up for alerts, save searches, etc.

PERSONAL SIGN IN

No SPIE Account? Create one

PURCHASE THIS CONTENT

SUBSCRIBE TO DIGITAL LIBRARY

50 downloads per 1-year subscription

Members: $195

Non-members: $335 ADD TO CART

25 downloads per 1 - year subscription

Members: $145

Non-members: $250 ADD TO CART

PURCHASE SINGLE ARTICLE

Includes PDF, HTML & Video, when available