Enhancement of plasmon-induced charge separation efficiency by coupling silver nanocubes with a thin gold film

[+] Author Affiliations
Kazutaka Akiyoshi, Koichiro Saito, Tetsu Tatsuma

University of Tokyo, Institute of Industrial Science, 4-6-1 Komaba, Meguro-ku, Tokyo 153-8505, Japan

J. Photon. Energy. 6(4), 042505 (Aug 09, 2016). doi:10.1117/1.JPE.6.042505
History: Received May 18, 2016; Accepted July 20, 2016
Text Size: A A A

Open Access Open Access

Abstract.  Plasmon-induced charge separation (PICS), in which an energetic electron is injected from a plasmonic nanoparticle (NP) to a semiconductor on contact, is often inhibited by a protecting agent adsorbed on the NP. We addressed this issue for an Ag nanocube-TiO2 system by coating it with a thin Au layer or by inserting the Au layer between the nanocubes (NCs) and TiO2. Both of the electrodes exhibit much higher photocurrents due to PICS than the electrodes without the Au film or the Ag NCs. These photocurrent enhancements can be explained in terms of PICS with accelerated electron transfer, in which electron injection from the Ag NCs or Ag@Au core-shell NCs to TiO2 is promoted by the Au film, or PICS enhanced by a nanoantenna effect, in which the electron injection from the Au film to TiO2 is enhanced by optical near field generated by the Ag NC.

Figures in this Article

Plasmonic light harvesting based on localized surface plasmon resonance (LSPR) of noble metal nanoparticles (NPs) has attracted much attention recently and is applied to photovoltaics and photocatalysis. There are two different ways of plasmonic light harvesting: (1) that based on a nanoantenna effect,1 in which a metal NP entraps a photon and transfers the obtained energy to a dye molecule or semiconductor via the optical near field generated in its vicinity, and (2) that based on plasmon-induced charge separation (PICS),2 in which an energetic electron is injected from a resonant NP to a semiconductor on contact. We reported PICS for the first time2 and indicated that it involves electron transfer from the plasmonic NPs to the semiconductor.27 The electron transfer involved is explained in terms of external photoelectric effect, hot electron injection, or interfacial electron transition, and recently some groups call it plasmonic hot electron (or carrier) injection. PICS has been widely applied to photovoltaics,2,812 photocatalysis,2,13,14 photochromism,1517 photoactuation,18 and chemical sensing.19

A wide variety of plasmonic NPs have been used for PICS such as nanospheres,20 nanoplates,7 and halfshell arrays.21 NPs prepared by photocatalytic deposition2 or thermal dewetting of an evaporated film9 are suitable for PICS because of direct contact with the semiconductor, while chemically synthesized NPs may exhibit lower charge separation efficiency since they are covered with a protective agent. In the case of Au nanorods (NRs) protected with cetyltrimethylammonium bromide in contact with a TiO2 thin film, we addressed the issue by photoelectrochemical deposition of Au from aqueous HAuCl4 at both ends of the NRs under UV irradiation for excitation of TiO2.22 The Au NRs were thus converted to nanodumbbells (NDs), and NDs exhibited improved efficiency of PICS-based electron transfer to TiO2 via the two spherical caps at both ends of NDs. Here, we propose an easier method to improve the PICS-based photocurrents. We use plasmonic Ag nanocubes (NCs) protected by poly(vinylpyrrolidone) (PVP) in this work. Although Ag NCs exhibit nanoantenna effects2325 and various interesting optical properties,2629 their PICS efficiency when they are in contact with TiO2 is low because of the insulating PVP layer. In the present work, in order to improve the PICS efficiency, we coupled the Ag NCs simply with an evaporated Au thin film, which is coated on the Ag NCs placed on TiO2 or coated directly on TiO2 as the underlayer of Ag NCs.

Preparation of Electrodes

Ag NCs were synthesized by the method reported by Im et al.30 with slight modifications28 [Fig. 1(a)]. The average edge length of the synthesized Ag NCs is about 80 nm. A transparent indium tin oxide (ITO) electrode was coated with a thin anatase TiO2 film (60-nm thick, observed by scanning electron microscopy, SEM) by a spray pyrolysis method at 500°C from 2-propanol containing 0.028 M titanium diisopropoxide bis(acetylacetonate) as a TiO2 precursor. The TiO2 film was irradiated with UV light in order to make the surface sufficiently hydrophilic. The synthesized Ag NCs were drop-cast onto the TiO2 surface (coverage 9×108  particlescm2). If necessary, the substrate was coated with an Au film (ca. 5-nm thick, measured by quartz crystal microbalance) by vacuum evaporation before or after the drop-casting [Fig. 1(b)]. Thus, we prepared four different electrodes: ITO/TiO2/Ag NC, ITO/TiO2/Ag NC/Au, ITO/TiO2/Au, and ITO/TiO2/Au/Ag NC (active area=12×20  mm).

Graphic Jump Location
Fig. 1
F1 :

Scanning electron micrographs of (a) the Ag NCs and (b) the Au films. (c) Extinction spectra of the ITO/TiO2/Ag NC, ITO/TiO2/Ag NC/Au, ITO/TiO2/Au, and ITO/TiO2/Au/Ag NC electrodes in water.

Measurement of Photocurrents

One of the four electrodes was used as the working electrode. This electrode was connected to a potentiostat (SI 1280 B, Solartron) with an Ag|AgCl reference electrode and a Pt counter electrode and soaked in 0.1 M aqueous KNO3 containing 0.5 M ethanol as an electron donor. The working electrode was polarized at +0.5  V versus Ag|AgCl and irradiated with monochromatic light (full width at half maximum=20  nm, 5.0×1015  photonscm2s1, and light irradiation area=1.8  cm2) using an optospectrum generator (Hamamatsu Photonics), and a steady-state photocurrent was measured at each wavelength. Virtually, the same photocurrents were observed even if the photoanode was short circuited to the counter electrode.

Photocurrent Responses of the ITO / TiO2 / Ag NC Electrode

Ag NCs dispersed in ethanol exhibit the main extinction peak based on dipolar LSPR at 506 nm. When an Ag NC is adsorbed onto a substrate with a high refractive index, the LSPR peak splits into two peaks due to the distal and proximal modes.26 In the distal mode, electron oscillation is localized at the top of the NC away from the substrate, and in the proximal mode, the oscillation is localized at the bottom of the NC in contact with the substrate. The Ag NCs on TiO2 show two peaks [Fig. 1(c)], namely peak A at 456 nm due to the distal mode and peak B at 530 nm due to the proximal mode.

First, we measured photocurrent responses from the ITO/TiO2/Ag NC electrode irradiated from the backside with monochromatic light of different wavelengths in the electrolyte solution. Three independently prepared electrodes were examined and the average currents were plotted against the irradiation wavelength (Fig. 2). Small anodic photocurrents were observed in the wavelength range examined (430 to 670 nm). Conduction electrons in an Ag NC oscillate in resonance with electric field oscillation of the incident light, and an electron is injected from the resonant NC to the conduction band of TiO2, resulting in PICS.2 As a result, the anodic photocurrent flows [Fig. 3(a)]. However, the photocurrents were very low and no obvious current peaks corresponding to the distal and proximal modes were obtained. The low currents could be explained in terms of a blocking effect of insulating PVP, which covers and protects the NC surface. Capping agents like PVP are known to block access of reactant molecules.31,32 Likewise, the PVP layer should also inhibit the electron transfer from the Ag NC to TiO2.

Graphic Jump Location
Fig. 2
F2 :

Photocurrent action spectra of the ITO/TiO2/Ag NC, ITO/TiO2/Ag NC/Au, ITO/TiO2/Au, and ITO/TiO2/Au/Ag NC electrodes in 0.1-M aqueous KNO3 containing 0.5-M ethanol. Each datapoint shows the average of photocurrent responses from three independently prepared electrodes.

Graphic Jump Location
Fig. 3
F3 :

Possible mechanisms of the photocurrents based on PICS for (a) ITO/TiO2/Ag NC, (b) ITO/TiO2/Au, and (c and d) ITO/TiO2/Ag NC/Au electrodes [(c) PICS with accelerated electron transfer and (d) PICS enhanced by the nanoantenna effect].

Effect of a Thin Gold Coating

We therefore coated the Ag NCs on TiO2 with a thin Au layer (ca. 5 nm thick) by evaporation, envisaging promotion of the electron transfer. The photocurrent responses from the ITO/TiO2/Ag NC/Au electrode thus prepared were measured and are shown in Fig. 2. The Au coating greatly improved the anodic photocurrents and a broad peak was obtained at around 550 nm. This electrode showed an extinction peak at 580 nm [Fig. 1(c)]. There is a possibility that the influence of the high refractive index substrate is weakened by the Au coating and therefore the distal mode is suppressed. The photocurrent response at the peak was about 20 times higher than that without the Au coating.

We also coated the Au layer directly on TiO2 and examined its photocurrent responses for comparison. This ITO/TiO2/Au electrode also exhibited photocurrent responses that increased gradually with increasing wavelength from about 500 nm. The extinction spectrum of the Au film showed a similar trend [Fig. 1(c)]. In general, a thin Au film prepared by evaporation consists of interconnected fine Au NPs, and hence it exhibits not only the propagating surface plasmon resonance, but also LSPR.33 Therefore, the present Au film also injects electrons into TiO2 and exhibits photocurrents based on PICS [Fig. 3(b)]. Actually, nanoparticulate structures of 10- to 20-nm size were observed by SEM [Fig. 1(b)]. With reference to the response of this electrode, the introduction of Ag NCs under the Au thin film enhanced the photocurrents by approximately five times.

Mechanisms of the Photocurrent Enhancement

There are two possible reasons that the response from the ITO/TiO2/Ag NC/Au electrode is much higher than those from the ITO/TiO2/Ag NC and ITO/TiO2/Au electrodes. One of them is “PICS with accelerated electron transfer” shown in Figs. 3(c) and 4(a), in which electron injection from the Ag NC or Ag@Au core-shell NC to TiO2 is promoted by good electronic contact between the Au film and TiO2. The other one is “PICS enhanced by the nanoantenna effect” shown in Figs. 3(d) and 4(b), in which the electron injection from Au to TiO2 is enhanced by optical near field generated by the Ag NC; the Ag NC absorbs light and generates optical near field in its vicinity, and then the Au film is efficiently excited by the near field (i.e., the nanoantenna effect2325) and causes PICS. In both cases, the current would be increased by increasing the amount of Ag NCs.34

Graphic Jump Location
Fig. 4
F4 :

Possible mechanisms of (a) the PICS with accelerated electron transfer and (b) PICS enhanced by the nanoantenna effect.

In order to obtain further information about the mechanisms of photocurrent enhancement, we prepared another type of electrode by drop-casting the Ag NCs onto the Au thin film coated directly on TiO2. The photocurrent action spectrum of the obtained ITO/TiO2/Au/Ag NC electrode was similar to that of the ITO/TiO2/Ag NC/Au electrode (Fig. 2), and a broad peak was observed at around 535 nm. The photocurrent enhancement factors at the peak wavelength are 23 and 5 with reference to the ITO/TiO2/Ag NC and the ITO/TiO2/Au electrodes, respectively. These photocurrent enhancements can also be explained in terms of both of the two possible mechanisms, namely the PICS with accelerated electron transfer and PICS enhanced by the nanoantenna effect. However, it is more likely that the Au thin film is excited by the optical near field of the NC proximal mode (i.e., the nanoantenna effect) because the PVP may also block the electron transfer from Ag NCs to the Au film.

Photocurrent responses based on PICS from the ITO/TiO2/Ag NC/Au and the ITO/TiO2/Au/Ag NC electrodes are much higher than those from the ITO/TiO2/Ag NC and ITO/TiO2/Au electrodes. These enhancements are likely due to PICS with accelerated electron transfer or PICS enhanced by the nanoantenna effect. These results would provide an easier way to improve PICS efficiency of photovoltaics, photocatalysis, and other systems with commercially available or chemically synthesized plasmonic NPs with protecting layers.

The authors are grateful to Gyu Min Kim for his help with immobilization of the NPs. This work was supported in part by a Grant-in-Aid for Scientific Research (Nos. 16H02082 and 16K14017) from the Japan Society for the Promotion of Science.

Atwater  H. A., and Polman  A., “Plasmonics for improved photovoltaic devices,” Nat. Mater.. 9, , 205 –213 (2010). 2040-3364 CrossRef 1476-1122 
Tian  Y., and Tatsuma  T., “Mechanisms and applications of plasmon-induced charge separation at TiO2 films loaded with gold nanoparticles,” J. Am. Chem. Soc.. 127, , 7632 –7637 (2005). 0002-7863 CrossRef
Sakai  N.  et al., “Plasmon resonance-based generation of cathodic photocurrent at electrodeposited gold nanoparticles coated with TiO2 films,” ChemPhysChem. 10, , 766 –769 (2009). 1439-4235 CrossRef
Tian  Y., and Tatsuma  T., “Plasmon-induced photoelectrochemistry at metal nanoparticles supported on nanoporous TiO2,” Chem. Commun.. 16, , 1810 –1811 (2004).CrossRef
Takahashia  Y., and Tatsuma  T., “Electrodeposition of thermally stable gold and silver nanoparticle ensembles through a thin alumina nanomask,” Nanoscale. 2, , 1494 –1499 (2010). 2040-3364 CrossRef
Yamaguchi  T.  et al., “Photoelectrochemical responses from polymer-coated plasmonic copper nanoparticles on TiO2,” Chem. Lett.. 41, , 1340 –1342 (2012). 0366-7022 CrossRef
Kazuma  E., and Tatsuma  T., “In-situ nanoimaging of photoinduced charge separation at the plasmonic Au nanoparticle-TiO2 interface,” Adv. Mater. Interfaces. 1, , 1400066  (2014).CrossRef
Yu  K., , Sakai  N., and Tatsuma  T., “Plasmon resonance-based solid-state photovoltaic devices,” Electrochemistry. 76, , 161 –164 (2008). 0305-9979 CrossRef
Takahashi  Y., and Tatsuma  T., “Solid state photovoltaic cells based on localized surface plasmon-induced charge separation,” Appl. Phys. Lett.. 99, , 182110  (2011). 0003-6951 CrossRef
Lee  Y. K.  et al., “Surface plasmon-driven hot electron flow probed with metal-semiconductor nanodiodes,” Nano Lett.. 11, , 4251 –4255 (2011). 1530-6984 CrossRef
Mubeen  S.  et al., “Plasmonic photosensitization of a wide band gap semiconductor: converting plasmons to charge carriers,” Nano Lett.. 11, , 5548 –5552 (2011). 1530-6984 CrossRef
Reineck  P.  et al., “A solid‐state plasmonic solar cell via metal nanoparticle self‐assembly,” Adv. Mater.. 24, , 4750 –4755 (2012). 0935-9648 CrossRef
Kowalska  E., , Abe  R., and Ohtani  B., “Visible light-induced photocatalytic reaction of gold-modified titanium(IV) oxide particles: action spectrum analysis,” Chem. Commun.. 241 –243 (2009).CrossRef
Tanaka  A., , Hashimoto  K., and Kominami  H., “Preparation of Au/CeO2 exhibiting strong surface plasmon resonance effective for selective or chemoselective oxidation of alcohols to aldehydes or ketones in aqueous suspensions under irradiation by green light,” J. Am. Chem. Soc.. 134, , 14526 –14533 (2012). 0002-7863 CrossRef
Ohko  Y.  et al., “Multicolor photochromism of TiO2 films loaded with Ag nanoparticles,” Nat. Mater.. 2, , 29 –31 (2003). 1476-1122 CrossRef
Kazuma  E., and Tatsuma  T., “Photoinduced reversible changes in morphology of plasmonic Ag nanorods on TiO2 and application to versatile photochromism,” Chem. Commun.. 48, , 1733 –1735 (2012).CrossRef
Tanabe  I., and Tatsuma  T., “Plasmonic manipulation of color and morphology of single silver nanospheres,” Nano Lett.. 12, , 5418 –5421 (2012). 1530-6984 CrossRef
Tatsuma  T., , Takada  K., and Miyazaki  T., “UV light-induced swelling and visible light-induced shrinking of a TiO2-containing redox gel,” Adv. Mater.. 19, , 1249 –1251 (2007). 0935-9648 CrossRef
Tatsuma  T.  et al., “Direct output of electrical signals from LSPR sensors on the basis of plasmon-induced charge separation,” Chem. Commun.. 51, , 6100 –6103 (2015).CrossRef
Yu  K., , Tian  Y., and Tatsuma  T., “Size effects of gold nanoparticles on plasmon-induced photocurrents of gold-TiO2 nanocomposites,” Phys. Chem. Chem. Phys.. 8, , 5417 –5420 (2006). 1463-9076 CrossRef
Wu  L., , Nishi  H., and Tatsuma  T., “Plasmon-induced charge separation at two-dimensional gold semishell arrays on SiO2@TiO2 colloidal crystals,” APL Mater.. 3, , 104406  (2015).CrossRef
Katagi  Y., , Kazuma  E., and Tatsuma  T., “Photoelectrochemical synthesis, optical properties and plasmon-induced charge separation behaviour of gold nanodumbbells on TiO2,” Nanoscale. 6, , 14543 –14548 (2014). 2040-3364 CrossRef
Baek  S.-W.  et al., “Au@Ag core-shell nanocubes for efficient plasmonic light scattering effect in low bandgap organic solar cells,” ACS Nano. 8, , 3302 –3312 (2014). 1936-0851 CrossRef
Kawawaki  T.  et al., “Efficiency enhancement of PbS quantum dot/ZnO nanowire bulk-heterojunction solar cells by plasmonic silver nanocubes,” ACS Nano. 9, , 4165 –4172 (2015). 1936-0851 CrossRef
Leonard  K.  et al., “Enhanced photoelectrochemical response of polythiophene photoelectrodes with controlled arrays of silver nanocubes,” J. Phys. Chem. C. 119, , 8829 –8837 (2015). 1932-7447 CrossRef
Sherry  L. J.  et al., “Localized surface plasmon resonance spectroscopy of single silver nanocubes,” Nano Lett.. 5, , 2034 –2038 (2005). 1530-6984 CrossRef
Moreau  A.  et al., “Controlled-reflectance surfaces with film-coupled colloidal nanoantennas,” Nature. 492, , 86 –89 (2012).CrossRef
Saito  K., and Tatsuma  T., “Asymmetric three-way plasmonic color routers,” Adv. Opt. Mater.. 3, , 883 –887 (2015). 2195-1071 CrossRef
Saito  K., and Tatsuma  T., “A transparent projection screen based on plasmonic Ag nanocubes,” Nanoscale. 7, , 20365 –20368 (2015).CrossRef
Im  S. H.  et al., “Large-scale synthesis of silver nanocubes: the role of HCl in promoting cube perfection and monodispersity,” Angew. Chem., Int. Ed.. 117, , 2192 –2195 (2005).CrossRef
Luo  M.  et al., “Facile removal of polyvinylpyrrolidone (PVP) adsorbates from Pt alloy nanoparticles,” J. Mater. Chem. A. 3, , 2770 –2775 (2015).CrossRef
Niu  Z., and Li  Y., “Removal and utilization of capping agents in nanocatalysis,” Chem. Mater.. 26, , 72 –83 (2014). 0897-4756 CrossRef
Gupta  R., , Dyer  M. J., and Weimer  W. A., “Preparation and characterization of surface plasmon resonance tunable gold and silver films,” J. Appl. Phys.. 92, , 5264 –5270 (2002). 0021-8979 CrossRef
Kawawaki  T., , Takahashi  Y., and Tatsuma  T., “Enhancement of PbS quantum dot-sensitized photocurrents by plasmonic gold nanoparticles,” J. Phys. Chem. C. 117, , 5901 –5907 (2013). 1932-7447 CrossRef

Kazutaka Akiyoshi is a PhD candidate in University of Tokyo, Japan. He received his BSc degree from Tokyo University of Science in 2014 and MSc from University of Tokyo in 2016. His research focuses mainly on development of photoelectrochemical devices based on plasmonic nanoparticles.

Koichiro Saito is a PhD candidate in University of Tokyo, Japan. He received his BSc in 2013 and MSc in 2015 degrees from University of Tokyo. His research focuses mainly on fabrication and photo-manipulation of plasmonic nanomaterials and application to photonic materials and devices.

Tetsu Tatsuma is a professor at University of Tokyo, Japan. He received his BSc in 1988, MSc in 1990, and PhD in 1993 degrees in electrochemistry from University of Tokyo. His current research interests include electrochemistry and plasmonics, in particular mechanistic analysis of plasmon-induced charge separation and its application to photovoltaics, photocatalysis, photochromism, sensors, and actuators.

© The Authors. Published by SPIE under a Creative Commons Attribution 3.0 Unported License. Distribution or reproduction of this work in whole or in part requires full attribution of the original publication, including its DOI.

Citation

Kazutaka Akiyoshi ; Koichiro Saito and Tetsu Tatsuma
"Enhancement of plasmon-induced charge separation efficiency by coupling silver nanocubes with a thin gold film", J. Photon. Energy. 6(4), 042505 (Aug 09, 2016). ; http://dx.doi.org/10.1117/1.JPE.6.042505


Figures

Graphic Jump Location
Fig. 4
F4 :

Possible mechanisms of (a) the PICS with accelerated electron transfer and (b) PICS enhanced by the nanoantenna effect.

Graphic Jump Location
Fig. 3
F3 :

Possible mechanisms of the photocurrents based on PICS for (a) ITO/TiO2/Ag NC, (b) ITO/TiO2/Au, and (c and d) ITO/TiO2/Ag NC/Au electrodes [(c) PICS with accelerated electron transfer and (d) PICS enhanced by the nanoantenna effect].

Graphic Jump Location
Fig. 2
F2 :

Photocurrent action spectra of the ITO/TiO2/Ag NC, ITO/TiO2/Ag NC/Au, ITO/TiO2/Au, and ITO/TiO2/Au/Ag NC electrodes in 0.1-M aqueous KNO3 containing 0.5-M ethanol. Each datapoint shows the average of photocurrent responses from three independently prepared electrodes.

Graphic Jump Location
Fig. 1
F1 :

Scanning electron micrographs of (a) the Ag NCs and (b) the Au films. (c) Extinction spectra of the ITO/TiO2/Ag NC, ITO/TiO2/Ag NC/Au, ITO/TiO2/Au, and ITO/TiO2/Au/Ag NC electrodes in water.

Tables

References

Atwater  H. A., and Polman  A., “Plasmonics for improved photovoltaic devices,” Nat. Mater.. 9, , 205 –213 (2010). 2040-3364 CrossRef 1476-1122 
Tian  Y., and Tatsuma  T., “Mechanisms and applications of plasmon-induced charge separation at TiO2 films loaded with gold nanoparticles,” J. Am. Chem. Soc.. 127, , 7632 –7637 (2005). 0002-7863 CrossRef
Sakai  N.  et al., “Plasmon resonance-based generation of cathodic photocurrent at electrodeposited gold nanoparticles coated with TiO2 films,” ChemPhysChem. 10, , 766 –769 (2009). 1439-4235 CrossRef
Tian  Y., and Tatsuma  T., “Plasmon-induced photoelectrochemistry at metal nanoparticles supported on nanoporous TiO2,” Chem. Commun.. 16, , 1810 –1811 (2004).CrossRef
Takahashia  Y., and Tatsuma  T., “Electrodeposition of thermally stable gold and silver nanoparticle ensembles through a thin alumina nanomask,” Nanoscale. 2, , 1494 –1499 (2010). 2040-3364 CrossRef
Yamaguchi  T.  et al., “Photoelectrochemical responses from polymer-coated plasmonic copper nanoparticles on TiO2,” Chem. Lett.. 41, , 1340 –1342 (2012). 0366-7022 CrossRef
Kazuma  E., and Tatsuma  T., “In-situ nanoimaging of photoinduced charge separation at the plasmonic Au nanoparticle-TiO2 interface,” Adv. Mater. Interfaces. 1, , 1400066  (2014).CrossRef
Yu  K., , Sakai  N., and Tatsuma  T., “Plasmon resonance-based solid-state photovoltaic devices,” Electrochemistry. 76, , 161 –164 (2008). 0305-9979 CrossRef
Takahashi  Y., and Tatsuma  T., “Solid state photovoltaic cells based on localized surface plasmon-induced charge separation,” Appl. Phys. Lett.. 99, , 182110  (2011). 0003-6951 CrossRef
Lee  Y. K.  et al., “Surface plasmon-driven hot electron flow probed with metal-semiconductor nanodiodes,” Nano Lett.. 11, , 4251 –4255 (2011). 1530-6984 CrossRef
Mubeen  S.  et al., “Plasmonic photosensitization of a wide band gap semiconductor: converting plasmons to charge carriers,” Nano Lett.. 11, , 5548 –5552 (2011). 1530-6984 CrossRef
Reineck  P.  et al., “A solid‐state plasmonic solar cell via metal nanoparticle self‐assembly,” Adv. Mater.. 24, , 4750 –4755 (2012). 0935-9648 CrossRef
Kowalska  E., , Abe  R., and Ohtani  B., “Visible light-induced photocatalytic reaction of gold-modified titanium(IV) oxide particles: action spectrum analysis,” Chem. Commun.. 241 –243 (2009).CrossRef
Tanaka  A., , Hashimoto  K., and Kominami  H., “Preparation of Au/CeO2 exhibiting strong surface plasmon resonance effective for selective or chemoselective oxidation of alcohols to aldehydes or ketones in aqueous suspensions under irradiation by green light,” J. Am. Chem. Soc.. 134, , 14526 –14533 (2012). 0002-7863 CrossRef
Ohko  Y.  et al., “Multicolor photochromism of TiO2 films loaded with Ag nanoparticles,” Nat. Mater.. 2, , 29 –31 (2003). 1476-1122 CrossRef
Kazuma  E., and Tatsuma  T., “Photoinduced reversible changes in morphology of plasmonic Ag nanorods on TiO2 and application to versatile photochromism,” Chem. Commun.. 48, , 1733 –1735 (2012).CrossRef
Tanabe  I., and Tatsuma  T., “Plasmonic manipulation of color and morphology of single silver nanospheres,” Nano Lett.. 12, , 5418 –5421 (2012). 1530-6984 CrossRef
Tatsuma  T., , Takada  K., and Miyazaki  T., “UV light-induced swelling and visible light-induced shrinking of a TiO2-containing redox gel,” Adv. Mater.. 19, , 1249 –1251 (2007). 0935-9648 CrossRef
Tatsuma  T.  et al., “Direct output of electrical signals from LSPR sensors on the basis of plasmon-induced charge separation,” Chem. Commun.. 51, , 6100 –6103 (2015).CrossRef
Yu  K., , Tian  Y., and Tatsuma  T., “Size effects of gold nanoparticles on plasmon-induced photocurrents of gold-TiO2 nanocomposites,” Phys. Chem. Chem. Phys.. 8, , 5417 –5420 (2006). 1463-9076 CrossRef
Wu  L., , Nishi  H., and Tatsuma  T., “Plasmon-induced charge separation at two-dimensional gold semishell arrays on SiO2@TiO2 colloidal crystals,” APL Mater.. 3, , 104406  (2015).CrossRef
Katagi  Y., , Kazuma  E., and Tatsuma  T., “Photoelectrochemical synthesis, optical properties and plasmon-induced charge separation behaviour of gold nanodumbbells on TiO2,” Nanoscale. 6, , 14543 –14548 (2014). 2040-3364 CrossRef
Baek  S.-W.  et al., “Au@Ag core-shell nanocubes for efficient plasmonic light scattering effect in low bandgap organic solar cells,” ACS Nano. 8, , 3302 –3312 (2014). 1936-0851 CrossRef
Kawawaki  T.  et al., “Efficiency enhancement of PbS quantum dot/ZnO nanowire bulk-heterojunction solar cells by plasmonic silver nanocubes,” ACS Nano. 9, , 4165 –4172 (2015). 1936-0851 CrossRef
Leonard  K.  et al., “Enhanced photoelectrochemical response of polythiophene photoelectrodes with controlled arrays of silver nanocubes,” J. Phys. Chem. C. 119, , 8829 –8837 (2015). 1932-7447 CrossRef
Sherry  L. J.  et al., “Localized surface plasmon resonance spectroscopy of single silver nanocubes,” Nano Lett.. 5, , 2034 –2038 (2005). 1530-6984 CrossRef
Moreau  A.  et al., “Controlled-reflectance surfaces with film-coupled colloidal nanoantennas,” Nature. 492, , 86 –89 (2012).CrossRef
Saito  K., and Tatsuma  T., “Asymmetric three-way plasmonic color routers,” Adv. Opt. Mater.. 3, , 883 –887 (2015). 2195-1071 CrossRef
Saito  K., and Tatsuma  T., “A transparent projection screen based on plasmonic Ag nanocubes,” Nanoscale. 7, , 20365 –20368 (2015).CrossRef
Im  S. H.  et al., “Large-scale synthesis of silver nanocubes: the role of HCl in promoting cube perfection and monodispersity,” Angew. Chem., Int. Ed.. 117, , 2192 –2195 (2005).CrossRef
Luo  M.  et al., “Facile removal of polyvinylpyrrolidone (PVP) adsorbates from Pt alloy nanoparticles,” J. Mater. Chem. A. 3, , 2770 –2775 (2015).CrossRef
Niu  Z., and Li  Y., “Removal and utilization of capping agents in nanocatalysis,” Chem. Mater.. 26, , 72 –83 (2014). 0897-4756 CrossRef
Gupta  R., , Dyer  M. J., and Weimer  W. A., “Preparation and characterization of surface plasmon resonance tunable gold and silver films,” J. Appl. Phys.. 92, , 5264 –5270 (2002). 0021-8979 CrossRef
Kawawaki  T., , Takahashi  Y., and Tatsuma  T., “Enhancement of PbS quantum dot-sensitized photocurrents by plasmonic gold nanoparticles,” J. Phys. Chem. C. 117, , 5901 –5907 (2013). 1932-7447 CrossRef

Some tools below are only available to our subscribers or users with an online account.

Related Content

Customize your page view by dragging & repositioning the boxes below.

Related Book Chapters

Topic Collections

PubMed Articles
Advertisement
  • Don't have an account?
  • Subscribe to the SPIE Digital Library
  • Create a FREE account to sign up for Digital Library content alerts and gain access to institutional subscriptions remotely.
Access This Article
Sign in or Create a personal account to Buy this article ($20 for members, $25 for non-members).
Access This Proceeding
Sign in or Create a personal account to Buy this article ($15 for members, $18 for non-members).
Access This Chapter

Access to SPIE eBooks is limited to subscribing institutions and is not available as part of a personal subscription. Print or electronic versions of individual SPIE books may be purchased via SPIE.org.