In this study, we focus on the precise control of electronic and ink properties for hole transport materials (HTM) and photoactive materials, consisting of p-type polymers (donors) and non-fullerene acceptors (NFA), to develop solution processable near-infrared (NIR) and short-wave infrared (SWIR) organic photodiodes(OPDs) with consistent performance over different batches. We observed fluctuations in the turn-on voltage of NIR-OPD devices when using different batches of our HTM. Regression analysis revealed a strong correlation between the turn-on voltage and specific factors in the polymer. By implementing an improved purification scheme, we successfully suppressed these fluctuations. Moreover, we investigated the impact of p-type polymer structure and properties on device performance and solubility in non-halogenated solvents. A trade-off between molecular weight and EQE of NIR-OPDs was identified in a commercially purchased polymer. However, by optimizing the synthesis pathway, we achieved compatibility between these parameters in our polymer and extended the ink storage period to over three months without compromising EQE and dark current. Additionally, we introduce a novel NFA, IR6, which exhibits an impressive EQE of 45% at 1100 nm with a dark current of 4 × 10 −5 mA/cm−2 . These advancements in precise material control and novel NFA offer promising prospects for the commercialization of solution-processable NIR-OPDs, making them viable candidates for high-performance near-infrared sensing applications.
We report ink formulations for solution-processable near-infrared organic photodiodes (OPDs) to fabricate organic CMOS image sensors on silicon wafers. The ink for the hole transport layer, which consists of cross-linkable semiconducting polymers, fully covers an 8-inch silicon wafer with less than 3 nm of variation in thickness by spin-coating. The ink is stable over several months. For the ink for the active layer, new additives are found to reduce micrometer size phase separation of donor and acceptor semiconductors after thermal annealing, which is fatal to achieve pixel to pixel reproducibility. Both inks are free from halogenated solvents.
Access to the requested content is limited to institutions that have purchased or subscribe to SPIE eBooks.
You are receiving this notice because your organization may not have SPIE eBooks access.*
*Shibboleth/Open Athens users─please
sign in
to access your institution's subscriptions.
To obtain this item, you may purchase the complete book in print or electronic format on
SPIE.org.
INSTITUTIONAL Select your institution to access the SPIE Digital Library.
PERSONAL Sign in with your SPIE account to access your personal subscriptions or to use specific features such as save to my library, sign up for alerts, save searches, etc.