Surface morphology of As-deposited and laser-damaged dielectric mirror coatings studied in-situ by atomic force microscopy

Mark R. Kozlowski; Michael C. Staggs; Mehdi Balooch; Robert J. Tench; Wigbert J. Siekhaus

doi:10.1117/12.134889

1 February 1992 Surface morphology of As-deposited and laser-damaged dielectric mirror coatings studied in-situ by atomic force microscopy

Mark R. Kozlowski, Michael C. Staggs, Mehdi Balooch, Robert J. Tench, Wigbert J. Siekhaus

Author Affiliations +

Proceedings Volume 1556, Scanning Microscopy Instrumentation; (1992) https://doi.org/10.1117/12.134889
Event: San Diego, '91, 1991, San Diego, CA, United States

Abstract

Atomic force microscopy was used to determine in situ the nanometer-scale morphological changes that occur on dielectric optical coatings as a result of laser-induced damage. The optical film studied was a highly reflective dielectric multilayer mirror (HR) consisting of many alternating HfO2 and SiO2 layers of quarter-wave thickness at 1.06 micrometers . The top layer was a (lambda) /2 SiO2 overcoat. Laser beam specifications were: 1.06 micrometers wavelength, 8 ns pulselength, and 110 micrometers to 300 micrometers beam diameter. The laser fluence was determined by beam profiling and total energy measurements. The maximum scan-range of the AFM was 80 micrometers . A survey of the as-deposited surface shows mostly hillocks of approximately 200 nm width and 10 nm height. Comparison of this hillock structure to that of a single layer of SiO2 and a surface layer of HfO2 was made. Irregularities (i.e., defects) on the surface of the HR consisted of micrometer-scale domes, and occasional craters, of micrometer planar dimension and depth extending over many layers. Three types of coating defects were identified which could be related to the classic nodule-type coating defect. Nodule defects were found to be easily ejected from the coating surface by laser illumination, leaving craters from which further damage would propagate. After laser damage with fluences above 30 J/cm2 the hillocks coalesced into structures with heights and widths 5 - 10 times that of the as-deposited film. A pattern of concentric surface distortions (ripples or cracks) appeared at higher fluences, in some cases following the full circumference of the beam.

Citation Download Citation

Mark R. Kozlowski, Michael C. Staggs, Mehdi Balooch, Robert J. Tench, and Wigbert J. Siekhaus "Surface morphology of As-deposited and laser-damaged dielectric mirror coatings studied in-situ by atomic force microscopy", Proc. SPIE 1556, Scanning Microscopy Instrumentation, (1 February 1992); https://doi.org/10.1117/12.134889

ACCESS THE FULL ARTICLE

INSTITUTIONAL
Select your institution to access the SPIE Digital Library.

SELECT YOUR INSTITUTION

PERSONAL
Sign in with your SPIE account to access your personal subscriptions or to use specific features such as save to my library, sign up for alerts, save searches, etc.

PERSONAL SIGN IN

No SPIE Account? Create one

;

PURCHASE THIS CONTENT

SUBSCRIBE TO DIGITAL LIBRARY

50 downloads per 1-year subscription

Members: $195

Non-members: $335 ADD TO CART

25 downloads per 1 - year subscription

Members: $145

Non-members: $250 ADD TO CART

PURCHASE SINGLE ARTICLE