8 November 2005 Evaluation of alternative capping layers for EUVL mask ML blank
Author Affiliations +
Abstract
The standard silicon (Si) capping layer used for extreme ultra-violet lithography (EUVL) multilayer (ML) mask blanks has some shortcomings, such as low oxidation resistance, low chemical resistance, low etch selectivity in either the SiO2 buffer layer etch to the capping layer or the absorber etch (e.g., TaN) to the capping layer. These performance and process issues with Si capped ML mask blank will reduce the mask lifetime and require tighter process control during EUVL mask fabrication. Alternative capping materials have been investigated for both EUVL optics and for mask applications.1-5 It has been initially demonstrated that Ru capping layers have high oxidation resistance and high mask process margin as compared to Si ML cap. In this paper, we will present a detailed evaluation of Ru and ion beam deposited (IBD) diamond-like-carbon (DLC) for EUVL mask application. Performance evaluations of the DLC mask blank capping layer and Ru capping layer were made in the area of reflectivity performance, shelf-life, and EUV exposure stability. It has been shown that EUV exposure induced capping layer change depends upon the exposure conditions. However, we found that as long as the induced relative change in the ML cap material are the same (e.g., the same amount of oxidation), regardless of exposure time and exposure conditions, the resulting reflectivity change is about the same. In the case of the two capping layer materials we evaluated, the capping surface reaction with active oxygen is the primary cause for the reflectivity degradation.
© (2005) COPYRIGHT Society of Photo-Optical Instrumentation Engineers (SPIE). Downloading of the abstract is permitted for personal use only.
Pei-yang Yan, Eberhard Spiller, Eric Gullikson, and Shannon Hill "Evaluation of alternative capping layers for EUVL mask ML blank", Proc. SPIE 5992, 25th Annual BACUS Symposium on Photomask Technology, 59923Z (8 November 2005); https://doi.org/10.1117/12.637599
Lens.org Logo
CITATIONS
Cited by 2 scholarly publications and 1 patent.
Advertisement
Advertisement
RIGHTS & PERMISSIONS
Get copyright permission  Get copyright permission on Copyright Marketplace
KEYWORDS
Reflectivity

Extreme ultraviolet lithography

Ruthenium

Photomasks

Ultraviolet radiation

Oxygen

Oxidation

RELATED CONTENT

EUV capping layer integrity
Proceedings of SPIE (June 12 2018)
Ru-capped EUVL ML mask blank performance
Proceedings of SPIE (August 20 2004)
EUVL mask with Ru ML capping
Proceedings of SPIE (December 17 2003)
Dry etching technologies for reflective multilayer
Proceedings of SPIE (November 08 2012)

Back to Top