Growth of short-period InAs/GaSb superlattices for mid-infrared photodetectors

H. J. Haugan; G. J. Brown; K. Mahalingam; S. Elhamri; W. C. Mitchel; L. Grazulis; J. M. Shank; S. Houston

doi:10.1117/12.680530

7 September 2006 Growth of short-period InAs/GaSb superlattices for mid-infrared photodetectors

H. J. Haugan, G. J. Brown, K. Mahalingam, S. Elhamri, W. C. Mitchel, L. Grazulis, J. M. Shank, S. Houston

Author Affiliations +

Proceedings Volume 6295, Infrared Detectors and Focal Plane Arrays VIII; 629502 (2006) https://doi.org/10.1117/12.680530
Event: SPIE Optics + Photonics, 2006, San Diego, California, United States

Abstract

The purpose of this work is to explore mid-infrared (IR) photodetector materials that can operate at room temperature. Shorter-period InAs/GaSb superlattices (SLs) have larger intervalance band seperations, which is beneficial for reducing Auger recombination and tunneling current, thus making room temperature operation possible. To test these possibilities, several short-period SLs ranging from 50 to 11 Å were designed for 4 μm detection threshold and molecular beam epitaxy was used to grow specially designed structures. Since morphological degradation is generally expected in shorter-period SLs, their structural qualities were monitored by transmission electron microscopy. The effect of layer properties on the optical and electrical properties was studied using low temperature photoconductivity measurements and magnetic field dependent Hall measurements. The samples with larger-periods (50 to 31 Å) showed excellent structural qualities, leading to sharper photoresponse band edge (5 meV) and lower residual background carrier concentrations (8x10¹⁰ cm^-2). As the period approached 24 Å, slight layer thickness undulations within the SLs were observed and these undulations intensified as the period further reduced to 17 Å. Evidently, these structural degradations strongly influence their optical properties causing significant broadening in photoresponse band edge (9 meV). In the thinner samples with the period below 17 Å, no optical signal was detected. With slower growth rates, samples with periods as thin as 19 Å were grown without significant layer thickness variations.

Citation Download Citation

H. J. Haugan, G. J. Brown, K. Mahalingam, S. Elhamri, W. C. Mitchel, L. Grazulis, J. M. Shank, and S. Houston "Growth of short-period InAs/GaSb superlattices for mid-infrared photodetectors", Proc. SPIE 6295, Infrared Detectors and Focal Plane Arrays VIII, 629502 (7 September 2006); https://doi.org/10.1117/12.680530

ACCESS THE FULL ARTICLE

INSTITUTIONAL
Select your institution to access the SPIE Digital Library.

SELECT YOUR INSTITUTION

PERSONAL
Sign in with your SPIE account to access your personal subscriptions or to use specific features such as save to my library, sign up for alerts, save searches, etc.

PERSONAL SIGN IN

No SPIE Account? Create one

;

PURCHASE THIS CONTENT

SUBSCRIBE TO DIGITAL LIBRARY

50 downloads per 1-year subscription

Members: $195

Non-members: $335 ADD TO CART

25 downloads per 1 - year subscription

Members: $145

Non-members: $250 ADD TO CART

PURCHASE SINGLE ARTICLE